HARRIS 15 Brazing Alloy Rod - 1/16 in - 5 lb | 015FC30

Brand: Harris Products
Manufacturer Part #: 

015FC30


Welding Supply Part Number: HWE015FC30
 /

  • Save 36%
    $220.80 $141.30 / Pack
  •  Standard Delivery
Sold in Packs of 5 LB

HARRIS 15 Brazing Alloy Rod - 1/16 in - 5 lb

HARRIS15 low fuming bronze is considered a "braze-welding" alloy as this copper/zinc alloy exhibits minimal capillary action during brazing. This limits joint design primarily to lap, tee, and butt joints. Butt joints require some edge preparation typically incorporating beveled edges to provide a location for filler metal to be applied and to ensure alloy penetration to the joint root. LFB was developed primarily to braze steel and some cast iron grades including malleable and grey iron. It can be used to join copper but due to its elevated melting temperature care must be taken during brazing to avoid overheating or melting the copper. It is used with the oxy-fuel process. These alloys are flux-coated.

Features

  • Copper-zinc braze-welding flux-coated rod
  • Flux coating provides excellent wetting action with no objectable fuming
  • Exhibits minimal capillary action during brazing
  • Limited joint designs to lap, tee and butt joints, although butt joints require some edge preparation
  • Good machinability
  • Produces porosity-free deposits
  • Color matches yellow brass
  • Developed to braze steel and some cast iron grades, including malleable and gray iron. Also, used to join copper
  • Corrosion resistance is similar to most high zinc brass alloys. Care should be taken on service conditions where water immersion is involved as dezincification is a potential issue

    • Brand Harris Products
    Container Size 5 lb
    Container Type Box
    Overall Length 18 in
    Series Harris 15
    Maximum Brazing Temperature 1750 °F
    MFG 015FC30
    Minimum Brazing Temperature 1670 °F

    Description

    HARRIS 15 Brazing Alloy Rod - 1/16 in - 5 lb

    HARRIS15 low fuming bronze is considered a "braze-welding" alloy as this copper/zinc alloy exhibits minimal capillary action during brazing. This limits joint design primarily to lap, tee, and butt joints. Butt joints require some edge preparation typically incorporating beveled edges to provide a location for filler metal to be applied and to ensure alloy penetration to the joint root. LFB was developed primarily to braze steel and some cast iron grades including malleable and grey iron. It can be used to join copper but due to its elevated melting temperature care must be taken during brazing to avoid overheating or melting the copper. It is used with the oxy-fuel process. These alloys are flux-coated.

    Features

  • Copper-zinc braze-welding flux-coated rod
  • Flux coating provides excellent wetting action with no objectable fuming
  • Exhibits minimal capillary action during brazing
  • Limited joint designs to lap, tee and butt joints, although butt joints require some edge preparation
  • Good machinability
  • Produces porosity-free deposits
  • Color matches yellow brass
  • Developed to braze steel and some cast iron grades, including malleable and gray iron. Also, used to join copper
  • Corrosion resistance is similar to most high zinc brass alloys. Care should be taken on service conditions where water immersion is involved as dezincification is a potential issue